extraction of copper from pcb
i soaked PCB in hcl solution for 2 month, suddenly when i mixed with h2o2 there is a brown bubble coming out and the solution turns into brown, what
chemical is this ( the PCB i used mostly from clf lamp)
|
|
|
macckone
International Hazard
Posts: 2159
Registered: 1-3-2013
Location: Over a mile high
Member Is Offline
Mood: Electrical
|
|
Copper is rather inert to HCl, however peroxide will make it much more reactive.
After 2 months you finally started to dissolve the copper.
However you will also dissolve other things that will not be as soluble.
Silver and lead have a small solubility and are usually considered insoluble
but they are soluble enough to separate from the pcb board under these conditions.
copper chloride complexes and be red, yellow or blue depending on the primary state.
They can also be a mixture which can give browns or greens.
The usual procedure is to add excess HCl and peroxide until the board is clean of copper.
Then filter to remove gunk, usually silver and lead.
Finally you plate the copper onto something.
|
|
|
phlogiston
International Hazard
Posts: 1375
Registered: 26-4-2008
Location: Neon Thorium Erbium Lanthanum Neodymium Sulphur
Member Is Offline
Mood: pyrophoric
|
|
Oxygen/air also can help dissolve the copper, but it is slow unless you actively bubble air through the solution.
Seems like a very elaborate way to recover a very small amount of copper.
-----
"If a rocket goes up, who cares where it comes down, that's not my concern said Wernher von Braun" - Tom Lehrer |
|
|
fusso
International Hazard
Posts: 1922
Registered: 23-6-2017
Location: 4 ∥ universes ahead of you
Member Is Offline
|
|
Quote: Originally posted by phlogiston  | Oxygen/air also can help dissolve the copper, but it is slow unless you actively bubble air through the solution.
Seems like a very elaborate way to recover a very small amount of copper. |
But not worth it since Cu content
isn't that high.
|
|
|
PyroPlatinum
Hazard to Self
Posts: 59
Registered: 21-2-2018
Member Is Offline
Mood: No Mood
|
|
Why would you like to do that other than etching circuit boards?
Copper is very easy to find...
|
|
|
Texium
|
Thread Moved
13-3-2024 at 05:31 |
![[*]](images/xpblue/default_icon.gif){kind=icon}