Getting extremely fine powder is a very big problem for a normal person. So to solve this problem i was thinking whether aluminium powder can be
formed by reacting aluminium with concentrated sulfuric acid then displacing it with magnesium . This method works for preparing zinc powder by
reacting it with hydrochloric acid then displacing it with magnesium. So i want to ask can aluminium powder can be prepared this way by reacting
aluminium with sulphuric acid then displacing it with magnesium.
|
|
|
woelen
Super Administrator
Posts: 7976
Registered: 20-8-2005
Location: Netherlands
Member Is Offline
Mood: interested
|
|
I never tried this myself, but I do not expect that this works. Aluminium is very reactive and easily reacts with water, when its oxide layer is
removed. You can see this reactivity if you take aluminium and add a solution of copper chloride or copper sulfate plus sodium chloride to it. This
mix destroys the oxide layer and then you see vigorous bubbling and formation of flocculent Al(OH)3 while it reacts with water.
|
|
|
Vikascoder
Hazard to Others
Posts: 309
Registered: 28-1-2012
Member Is Offline
Mood: No Mood
|
|
I think it would works . Because when i had tried this method i got extremely fine powder aluminium though i have not tested it till now. By the way
industrially how german dark head black aluminium powder is formed.
|
|
|
Adas
National Hazard
Posts: 711
Registered: 21-9-2011
Location: Slovakia
Member Is Offline
Mood: Sensitive to shock and friction
|
|
German dark Al also contains 5% of carbon to enhance its performance. Probably you can make Al this way, if it doesn't react too fast with water.
And reacting Al with H2SO4 is rather a slow process, buy some Al2(SO4)3 instead.
Rest In Pieces!
|
|
|
barley81
Hazard to Others
Posts: 481
Registered: 9-5-2011
Member Is Offline
Mood: No Mood
|
|
There is a tutorial on instructables for making aluminum powder. Shredded Al foil and charcoal are put into a rock tumbler with steel marbles for
several days. After sieving, I got a moderately fine powder that burned very brightly when lit using a torch. I have no way of measuring particle
size, though.
Sorry if this is OT. I thought it might be useful.
[Edited on 3-5-2012 by barley81]
|
|
|
Neil
National Hazard
Posts: 556
Registered: 19-3-2008
Member Is Offline
Mood: No Mood
|
|
Steel bearings may spark, that would be bad...
Check out the posts by 'the wizard is in'. He laid out safety data and bemoaned the dangers of a spark in a drum of powdered aluminum on several
occasions.
|
|
|
barley81
Hazard to Others
Posts: 481
Registered: 9-5-2011
Member Is Offline
Mood: No Mood
|
|
Ooh. I should've done some research last year before going ahead with that. Most of the aluminum was really coarse because of the way I shredded it.
In that case, lead/antimony non-sparking media would be better.
|
|
|
lagerdale
Harmless
Posts: 4
Registered: 6-5-2012
Member Is Offline
Mood: No Mood
|
|
Quote: Originally posted by woelen  | | I never tried this myself, but I do not expect that this works. Aluminium is very reactive and easily reacts with water, when its oxide layer is
removed. You can see this reactivity if you take aluminium and add a solution of copper chloride or copper sulfate plus sodium chloride to it. This
mix destroys the oxide layer and then you see vigorous bubbling and formation of flocculent Al(OH)3 while it reacts with water.
|
Isn't that what mercuric chloride also do to aluminum?
If yes, why do people use toxic mercuric chloride to strip the oxide layer of aluminium, instead of safe copper chloride?
|
|
|
DougTheMapper
Hazard to Others
Posts: 145
Registered: 20-7-2008
Location: Michigan, USA
Member Is Offline
Mood: Energetic
|
|
What about the thermal decomposition of aluminum oxalate?
FeC2O4 decomposes easily with heat to extremely fine Fe and CO2 - so fine, in fact, that it's pyrophoric.
I wonder if Al could behave the same way. On the other hand, Mg has sufficient reduction potential to strip O from CO2 so the same could be said about
aluminum. However, IIRC the decomposition of oxalates are generally at lower temperatures than, say, the ignition temperature of aluminum in oxygen.
Then again, it might be fine eno9ugh to be pyrophoric.
I am about to go to bed but I will try this tomorrow after work and see what happens, and whether Al will react directly with oxalic acid (It may
passivate it; it's used for anodizing) or if I'm going to have to make some AlCl3 (Al dissolved in HCl) in solution first, add the oxalic acid, and
heat to remove HCl. We shall see.
I have doubts about this method though... aluminum oxalate occurs as a tetrahydrate and the water of crystallization might destroy the hot aluminum
powder.
[Edited on 7-5-2012 by DougTheMapper]
Victor Grignard is a methylated spirit.
|
|
|
AndersHoveland
Hazard to Other Members, due to repeated speculation and posting of untested highly dangerous procedures!
Posts: 1986
Registered: 2-3-2011
Member Is Offline
Mood: No Mood
|
|
| Quote: Originally posted by Vikascoder | | i was thinking whether aluminium powder can be formed by reacting aluminium with concentrated sulfuric acid then displacing it with magnesium.
|
If you intend the aluminum powder for pyrotechnic use, and have magnesium, there is a more practical route.
A mixture of aluminum and magnesium can be melted in a steel container, without much difficulty, using a propane torch applied underneath. This forms
a brittle "magnalium" alloy, which can then be hammered into a fine powder. Magnalium has many of the advantages of magnesium, while being much more
resistant to corrosion, for use in pyrotechnics.
|
|
|
woelen
Super Administrator
Posts: 7976
Registered: 20-8-2005
Location: Netherlands
Member Is Offline
Mood: interested
|
|
| Quote: Originally posted by Vikascoder | | I think it would works . Because when i had tried this method i got extremely fine powder aluminium though i have not tested it till now. By the way
industrially how german dark head black aluminium powder is formed. |
Are you sure about that? Could you
please provide us with a reference or link which elaborates on this? I am very doubtful about your claim. You did not test your powder, so that is the
first you need to do and you also have to show that it really is aluminium and not unreacted magnesium powder. At this moment I am not yet convinced,
but I remain open for new ideas.
|
|
|
bbartlog
International Hazard
Posts: 1139
Registered: 27-8-2009
Location: Unmoored in time
Member Is Offline
Mood: No Mood
|
|
| Quote: Originally posted by DougTheMapper | What about the thermal decomposition of aluminum oxalate?
FeC2O4 decomposes easily with heat to extremely fine Fe and CO2 - so fine, in fact, that it's pyrophoric.
I wonder if Al could behave the same way.
[Edited on 7-5-2012 by DougTheMapper] |
No. Aluminum is too readily oxidized for this to work. The pyrolysis of some transition metal oxalates does yield (some) elemental metal (nickel,
silver, iron, copper at least), but from aluminum oxalate you get alumina. Not a bad way to prepare finely divided alumina, as a search on 'pyrolysis
of aluminum oxalate' will inform you, but useless as a way to aluminum powder.