kazaa81
Hazard to Others
Posts: 368
Registered: 30-4-2004
Member Is Offline
Mood: ok
|
|
Identify a mineral. Help needed!
Hallo to all,
I've bought a mineral, shiny brillant and metallic to apparence.
It is quite heavy (density probably > 5g/cm3).
It is somewhat granular to touch and eyes, abrasive. It is iron-like color, but much brillant, shiny.
I've tried to dissolve a small piece of it in 90% H2SO4 but nothing happened, and the pieces hadn't dissolved.
Can anyone help me to identify this mineral? For example a test to do on it, some minerals which are like my description. I haven't a camera, so
I can't post any photo.
Thanks at all for help! 
|
|
|
Esplosivo
Hazard to Others
Posts: 491
Registered: 7-2-2004
Location: Mediterranean
Member Is Offline
Mood: Quantized
|
|
Galena maybe? Try reacting a small piece with hot/warm HCl. Being lead sulfide, H2S should be given off (odour) and it should dissolve quite well, the
soln ppting white crystals when cooled due to the low solubility of PbCl2.
Theory guides, experiment decides.
|
|
|
kazaa81
Hazard to Others
Posts: 368
Registered: 30-4-2004
Member Is Offline
Mood: ok
|
|
Thanks very much...
Hi,
thanks Esplosivo!
It isn't galena (PbS), really!
I've tried what you've post, but doesn't happened anything. I've some galena and it doesn't have any properties similar to
the mineral I'm talking about.
For example PbS is something soft, this mineral is hard, much hard that, when I was trying to get a small piece from it with a 100g hammer, the
hammer's edges became rounded.
Thanks at all for help.
|
|
|
Twospoons
International Hazard
Posts: 1282
Registered: 26-7-2004
Location: Middle Earth
Member Is Offline
Mood: A trace of hope...
|
|
Haematite? Try abrading with very fine wet sandpaper (like 1000 grit). Haematite with give a dark blood red colour to the wet paper.
|
|
|
12AX7
Post Harlot
Posts: 4803
Registered: 8-3-2005
Location: oscillating
Member Is Offline
Mood: informative
|
|
Hmm, ain't silicon (polycrystalline), carbon of any sort, a carbide perhaps? Man-made? Possibly a ferroalloy (ferrosilicon, ferrochromium,
etc.)?
Tim
|
|
|
Saerynide
National Hazard
Posts: 954
Registered: 17-11-2003
Location: The Void
Member Is Offline
Mood: Ionic
|
|
I was about to suggest silicon as well. If its very shiny, with a bluish silver tinge, it very well could be Si. Si lumps are quite dense and hard.
"Microsoft reserves the right at all times to monitor communications on the Service and disclose any information Microsoft deems necessary to...
satisfy any applicable law, regulation or legal process"
|
|
|
chemoleo
Biochemicus Energeticus
Posts: 3005
Registered: 23-7-2003
Location: England Germany
Member Is Offline
Mood: crystalline
|
|
How about a Bismuth crystal? There's a thread on it, this should help with you the analysis.
Also I suggest a density measurement - weigh the piece, and then drop it into a graded measuring cylinder, and see how much volume it displaces, and
calculate the density from it.
Bi has a high density.
Never Stop to Begin, and Never Begin to Stop...
Tolerance is good. But not with the intolerant! (Wilhelm Busch)
|
|
|
neutrino
International Hazard
Posts: 1583
Registered: 20-8-2004
Location: USA
Member Is Offline
Mood: oscillating
|
|
Nope, bismuth is very soft and weak. You can easily break plates a couple of mm thick with your hands.
|
|
|
chemoleo
Biochemicus Energeticus
Posts: 3005
Registered: 23-7-2003
Location: England Germany
Member Is Offline
Mood: crystalline
|
|
Sure. The crystals are hard though. The surface is hard too. The Bi I got is a big fat bar that is certainly not bendable easily. Anyway..
Kazaa, try and melt a little bit under the flame. What happens?
Never Stop to Begin, and Never Begin to Stop...
Tolerance is good. But not with the intolerant! (Wilhelm Busch)
|
|
|
neutrino
International Hazard
Posts: 1583
Registered: 20-8-2004
Location: USA
Member Is Offline
Mood: oscillating
|
|
Both my ingots and the crystals I grew are rather soft; I can dent the stuff with my fingernail. This doesn’t exactly match up with the damaged
hammer thing. The difference is that my bismuth is 99.99% pure, while his would be much lower due to being a raw mineral. Would the impurities
strengthen the metal that much?
|
|
|
kazaa81
Hazard to Others
Posts: 368
Registered: 30-4-2004
Member Is Offline
Mood: ok
|
|
Density of mineral....
Hallo to all,
I've measured the density of my mineral by placing it in a graduated box with water, weighted, and measured the volume occuped.
The density has resulted something 3,7-4,0 g per cm^3.
Hope that this help. Thanks at all!
|
|
|
Saerynide
National Hazard
Posts: 954
Registered: 17-11-2003
Location: The Void
Member Is Offline
Mood: Ionic
|
|
I havent been able to find the density of crystalline Si, so I dunno whether the density matches.
Heres some pics of Si crystals:
or
"Microsoft reserves the right at all times to monitor communications on the Service and disclose any information Microsoft deems necessary to...
satisfy any applicable law, regulation or legal process"
|
|
|
12AX7
Post Harlot
Posts: 4803
Registered: 8-3-2005
Location: oscillating
Member Is Offline
Mood: informative
|
|
AFAIK, silicon is close to aluminum, just a little over (SG = 3 or so). It's a little darker than most shiny metals and definetly glassy, though
that may be missed on polycrystalline samples (most Si you'll find was probably a chunk (hence either polished, or conchoidal fracture) of a
99.9999% boule).
3.7 to 4 sounds a bit heavy. Do you have a picture? Mohs hardness test? Streak test?
Tim
|
|
|
Minus459F
Harmless
Posts: 3
Registered: 14-3-2005
Member Is Offline
Mood: No Mood
|
|
To Kazaa
I'm not sure, but I suspect what you have is an iron concretion. I picked up some several years ago and marveled at the weight of them. Very
hard. I happen to know a minerologist and took the sample to him. Nothing special, just something that happens in water sometimes. If you can find
enough of it you can sell it as iron ore.
To see if you have the same thing I had, use a grinder and try to grind away a portion of it (this is not really easy to do). The ground surface will
be shiny, as if you had ground away iron, but it will not look exactly (but close) like iron in color and reflectivity because of the silicates in the
matrix.
|
|
|
![[*]](images/xpblue/default_icon.gif){kind=icon}