RogueRose
International Hazard
Posts: 1585
Registered: 16-6-2014
Member Is Offline
|
|
Non-reactant material to cool moulten NaOH on
I've never worked with molten lye before so I'm a little out of my element here and don't know its behavior in this state and temp.
I need some suggestions of a material on which to pour moulten lye onto after it is used as a cleaning dip. I would think that Al would be out of the
question and I have a feeling that glass may be as well.
I plan on using a stainless steel pot to heat the lye and I suspect that may be the only readily available material which can withstand hot lye.
I'd like to be able to pour the lye into a thin sheet so it can be broken up later, thick pieces will make for messy and dangerous break-up.
Any suggestions on how to handle this
|
|
|
DraconicAcid
International Hazard
Posts: 4278
Registered: 1-2-2013
Location: The tiniest college campus ever....
Member Is Offline
Mood: Semi-victorious.
|
|
Teflon, as long as it's not too hot.
Please remember: "Filtrate" is not a verb.
Write up your lab reports the way your instructor wants them, not the way your ex-instructor wants them.
|
|
|
Metacelsus
International Hazard
Posts: 2531
Registered: 26-12-2012
Location: Boston, MA
Member Is Offline
Mood: Double, double, toil and trouble
|
|
Copper would also work, and would tolerate higher temperatures. This goes without saying, but use caution when pouring molten NaOH.
|
|
|
BromicAcid
International Hazard
Posts: 3227
Registered: 13-7-2003
Location: Wisconsin
Member Is Offline
Mood: Rock n' Roll
|
|
Where did you get this information from? Teflon reacts readily with molten sodium hydroxide, interestingly enough, molten sodium hydroxide is one of
the few chemicals often listed as being reactive with PTFE. Not only that but NaOH melts at 318C, whereas teflon starts to break down at 260C
(depending on the source) so double-whammy.
@RogueRose: There are some pointers in the sodium thread, nickel is the metal of choice. I personally have had good luck with cast iron (though with
slight discoloration). As for stainless and copper I cannot say with any certainty, I had thought that once upon a time I had evaluated using
stainless prior to settling on cast iron and had to change my mind due to compatibility but I cannot point to anything concrete.
|
|
|
DraconicAcid
International Hazard
Posts: 4278
Registered: 1-2-2013
Location: The tiniest college campus ever....
Member Is Offline
Mood: Semi-victorious.
|
|
Quote: Originally posted by BromicAcid  |
Where did you get this information from? Teflon reacts readily with molten sodium hydroxide, interestingly enough, molten sodium hydroxide is one of
the few chemicals often listed as being reactive with PTFE. Not only that but NaOH melts at 318C, whereas teflon starts to break down at 260C
(depending on the source) so double-whammy.
|
A research paper I wrote on using molten salts as solvents many, many years ago. I may very well have misremembered.
Please remember: "Filtrate" is not a verb.
Write up your lab reports the way your instructor wants them, not the way your ex-instructor wants them.
|
|
|
macckone
International Hazard
Posts: 2159
Registered: 1-3-2013
Location: Over a mile high
Member Is Offline
Mood: Electrical
|
|
Nickel is used industrially. Steel should also work. Teflon is definitely a no.
|
|
|
S.C. Wack
bibliomaster
Posts: 2419
Registered: 7-5-2004
Location: Cornworld, Central USA
Member Is Offline
Mood: Enhanced
|
|
Cast iron is fine but...Nickel foil on ebay!!! Not too expensive...and a cookie sheet...or just the cookie sheet.
[Edited on 17-4-2016 by S.C. Wack]
|
|
|
j_sum1
Administrator
Posts: 6218
Registered: 4-10-2014
Location: Unmoved
Member Is Offline
Mood: Organised
|
|
Of all the things currently sitting around in my lab, I would probably either try a cast iron dish I have or a graphite slab which I don't think would
present any hazards.
What sort of crucible are you using for heating it? Any reason why you wouldn't use the same material?
|
|
|
Sulaiman
International Hazard
Posts: 3554
Registered: 8-2-2015
Location: 3rd rock from the sun
Member Is Offline
|
|
I guess that an oven-dried pre-heated ceramic tile would work well.
|
|
|
hyfalcon
International Hazard
Posts: 1003
Registered: 29-3-2012
Member Is Offline
Mood: No Mood
|
|
As long as that tile isn't glazed. Molten NaOH will treat the glaze on ceramic just like glass.
Try a pizza stone.
[Edited on 18-4-2016 by hyfalcon]
|
|
|
macckone
International Hazard
Posts: 2159
Registered: 1-3-2013
Location: Over a mile high
Member Is Offline
Mood: Electrical
|
|
I would recommend against ceramics. The common ones are alumina silica mixtures readily contaminating sodium hydroxide. Use metal, although aluminum
is a poor choice.
|
|
|
Amos
International Hazard
Posts: 1406
Registered: 25-3-2014
Location: Yes
Member Is Offline
Mood: No
|
|
I will second the suggestion not to use ceramic. Clean a stainless steel surface USING molten sodium hydroxide first and then it should be able to
contain it without reacting.
|
|
|