Strontium Ferrite?
I'm interested in making some Strontium ferrite for BIG transformer cores. Anybody have any info on how it's made? I'm having trouble getting good
resources.
If anyone knows of an easier to make or obtain core material I'd be interested in hearing about it.
|
|
|
12AX7
Post Harlot
Posts: 4803
Registered: 8-3-2005
Location: oscillating
Member Is Offline
Mood: informative
|
|
Should be something like, make a slip or whatever of ball-milled SrO and Fe2O3 (as SrFe2O4? Not to suggest spinel of course, as I recall spinels only
form with the smaller ions i.e. Mg, Fe(II), etc.). A gum binder or such will be needed since this isn't clay. 99% purity should be good. Press or
cast to shape, dry, and sinter (fire) to something just below the melting point.
I didn't know strontium ferrites were used. I have heard only transition metals like manganese and zinc. I forget which ones are the hard ferrites
(i.e. ceramic magnets).
Overall this is going to be more trouble than buying, especially if you want a 100kW core or something. It'll take days to fire something that big
without cracking, and you just don't have the process control, chemical or thermal, that industry has.
If you do go through with this, I would love to get a sample of a typical product though!
Tim
|
|
|
Mr. Wizard
International Hazard
Posts: 1042
Registered: 30-3-2003
Member Is Offline
Mood: No Mood
|
|
You can get Strontium Nitrate from red road flares, although I'm sure it's not pure. You'de have to remove the oils, the wood flour and the Sulfur.
|
|
|
tumadre
Hazard to Others
Posts: 171
Registered: 10-5-2005
Member Is Offline
Mood: No Mood
|
|
the temperatures required are very high,
I would say use what is already avalible, grind it up and use a small amount of binder and fire it, or grind into power and mix with epoxy, but that
would be like a powerded iron core, not what you want?
|
|
|
not_important
International Hazard
Posts: 3873
Registered: 21-7-2006
Member Is Offline
Mood: No Mood
|
|
having troubles getting my reply to post, trying fragments
hmmm, it looks as if
http://www.hoosiermagneticsinc.com will sell ferrite powders
|
|
|
not_important
International Hazard
Posts: 3873
Registered: 21-7-2006
Member Is Offline
Mood: No Mood
|
|
while making them is discussed in many places, including
http://www.blackwell-synergy.com/doi/abs/10.1111/j.1151-2916...
http://cat.inist.fr/?aModele=afficheN&cpsidt=13664922
http://www.springerlink.com/content/b866j67715625473/
Either precipitation or prolonged ball milling, if not both, looks to be needed. Also appears than firing at 600 to 1200 C is needed.
|
|
|
not_important
International Hazard
Posts: 3873
Registered: 21-7-2006
Member Is Offline
Mood: No Mood
|
|
and the last URL, after finding one to the same reference, and that doesn't choke the forum software
http://www.ingentaconnect.com/content/ap/cs/2001/00000236/00...
|
|
|
tumadre
Hazard to Others
Posts: 171
Registered: 10-5-2005
Member Is Offline
Mood: No Mood
|
|
even if you achieve %85 or %90 the density achieved by the same ferrite product produced by industry, the magnetic properties will be vastly
different.
so unless there is nothing fundamentaly different between industry and DIY ferrite production, your not going to have good magnetic qualities.
|
|
|