Help needed re: metals or compounds that glow
I have recently come across a problem I wish to solve. I am trying to find a metal, mineral, or compound that will glow very brightly when flame is
applied but will NOT vaporize rapidly. It must be able to be formed into various shapes or rods. It must be stable, safe, and non-toxic before,
during, and after the application of flame/heat.
In which forum subsection would I best be served asking about this?
Thanks for your help. I will check back later but for now, I will go back to doing what I do best. Griping at my college students!
[Edited on 16-6-2012 by Papa Smoke]
|
|
|
plante1999
International Hazard
Posts: 1936
Registered: 27-12-2010
Member Is Offline
Mood: Mad as a hatter
|
|
Calcium oxide with a glassing on top?
I never asked for this.
|
|
|
Wizzard
Hazard to Others
Posts: 337
Registered: 22-3-2010
Member Is Offline
Mood: No Mood
|
|
SiC fibers COULD be used, like whiskers, but you'd need to protect them from any physical contact- They are VERY thin!
http://en.wikipedia.org/wiki/Thin_filament_pyrometry
|
|
|
Zan Divine
Hazard to Others
Posts: 170
Registered: 3-12-2011
Location: New York
Member Is Offline
Mood: Wishing all the worst that life has to offer to that SOB Wayne Lapierre
|
|
Molybdenum disilicide?
There are many commercial suppliers of formed "Moly DiSi"
heating elements. Therefore fabrication problems have already been addressed. These operate @ 1700 C in furnaces and are resistant to oxidation. They
are costly, however.
Since the criteria you specify are grossly similar to those of the heating element industry (ability to form into thin cross-sectional forms and
ability to operate in a region where blackbody radiation means things glow), this is a good area to mine.
As to metal options, you can purchase platinum coated tungsten wire commercially. It resists oxidation very well and tolerates very high temps. If
your needs are not that demanding, there are any number of cheaper resistance heating formulations.
[Edited on 16-6-2012 by Zan Divine]
He who makes a beast of himself gets rid of some of the pain of being a man. --HST
|
|
|
chornedsnorkack
National Hazard
Posts: 521
Registered: 16-2-2012
Member Is Offline
Mood: No Mood
|
|
Among metals, the highest temperature tolerance in air or oxidizing flame is iridium - the only metal that endures over 2000 Celsius. All transition
metals from tantalum to osmium form volatile oxides, and platinum melts at 1750 Celsius.
Among oxides, high melting point is possessed by, e. g. thoria, zirconia, ceria, magnesia, quicklime. These are generally brittle, though, so they may
be vulnerable to crumbling away.
|
|
|
dann2
International Hazard
Posts: 1523
Registered: 31-1-2007
Member Is Offline
Mood: No Mood
|
|
Plant1999 Suggested using the 'lime light' as it was called when used way back in the day for stage shows.
Sounds like a good solution.
|
|
|
phlogiston
International Hazard
Posts: 1375
Registered: 26-4-2008
Location: Neon Thorium Erbium Lanthanum Neodymium Sulphur
Member Is Offline
Mood: pyrophoric
|
|
Zinc oxide and cerium oxide also exhibit 'candoluminesence', like CaO.
Thorium oxide is well known for its use in gass mantles, but it also radioactive and therefore doesn't match your requirements.
-----
"If a rocket goes up, who cares where it comes down, that's not my concern said Wernher von Braun" - Tom Lehrer |
|
|
Papa Smoke
Harmless
Posts: 2
Registered: 16-6-2012
Member Is Offline
Mood: No Mood
|
|
Thanks all! Wow! I have LOTS of experimenting to do (some of it quite expensive!!)
I am trying to find the wire, etc. that glows the brightest and is destroyed the slowest by fire.
Should be great fun!!!
|
|
|
Neil
National Hazard
Posts: 556
Registered: 19-3-2008
Member Is Offline
Mood: No Mood
|
|
Yitrium oxide and MgO from heated MgSO4 work well.
A wire? Platinum.
|
|
|
RadioTrefoil
Harmless
Posts: 16
Registered: 11-7-2012
Location: New Zealand
Member Is Offline
Mood: Inert
|
|
Platinum wire! Heat it up and then dangle it over a flask with ammonia solution in the bottom, it will glow bright red hot for ages and will not be
damaged AT ALL because it is acting as a catalyst for oxidation of the ammonia gas. It will only stop glowing when there is no more ammonia or oxygen
left.
MESITYL FREAKING OXIDE
|
|
|
barley81
Hazard to Others
Posts: 481
Registered: 9-5-2011
Member Is Offline
Mood: No Mood
|
|
The mineral fluorite (CaF<sub>2</sub> is thermoluminescent and glows
when heated. It is safe, non-toxic, and stable; however, it cannot easily be formed into shapes. A jeweler may be able to take large crystals and
grind them down to the shape you want.
EDIT: this happens if the fluorite has been exposed to ionizing radiation. The energy is released when the fluorite is heated.
[Edited on 18-7-2012 by barley81]
|
|
|
polymerizer87
Harmless
Posts: 35
Registered: 16-7-2012
Member Is Offline
Mood: No Mood
|
|
Fireflies
Look up "luciferin" the compound in fireflies that makes them glow. Not sure how you would synthesize this considering it's an enzymatic process.
|
|
|
![[*]](images/xpblue/default_icon.gif){kind=icon}