Sometimes I melt (stainless) steel using a DC arc welder with carbon rods. But after melting, the steel gets brittle as it absorbs carbon and
transforms to cast iron. Once I used thick steel wire embedded in refractory cement ending in the bottom of the cavity where the steel is to be
melted. That works, I connect the steel wire to the anode and use a carbon rod as cathode. So, when the steel is molten, the steel bath acts as anode.
But, yet the metal gets brittle as well.
Might be tungsten rods can be a solution, but W also oxidizes quickly at steel melt temperatures.
Commercial EAF melt shops in steel industry use C rods as well, but they have much better control over the composition of the steel bath.
Does anybody have ideas / experiences ?
|
|
|
mysteriusbhoice
Hazard to Others
Posts: 477
Registered: 27-1-2016
Member Is Offline
Mood: Became chemistry catboy Vtuber Nyaa
|
|
if you have inert gas you can probably use tungsten as your electrode
|
|
|
Rainwater
National Hazard
Posts: 801
Registered: 22-12-2021
Member Is Offline
Mood: indisposition to activity
|
|
O2 is blown into the melt which produces CO that bubbles out of the mix. Any Fe that reacts first to form oxides will be reduced back into metal by
the carbon content.
Its a secret process for each manufacturer so the exact details are hard to obtain and are batch dependent
"You can't do that" - challenge accepted
|
|
|
Twospoons
International Hazard
Posts: 1284
Registered: 26-7-2004
Location: Middle Earth
Member Is Offline
Mood: A trace of hope...
|
|
Are you sure its not just the fact that its cast thats resulting in brittleness? Typical steels get tougher through hot or cold working, then
tempering. You dont get that with a casting.