angela_li
Harmless
Posts: 8
Registered: 3-12-2007
Member Is Offline
Mood: No Mood
|
|
Dark Green water
Hi All.
My expeiment: I am milling the oxide and sulphide ore down to micron's and not heap leaching. I am using a agitation leaching at 1-1.5% sulf acid,
then pass through LIX with 2 extraction phase and 1 stripping phase. At the EW stage should I be using 15 or 18% sulf acid.
Sorry I forgot to mention the ore also contain Silver and Lead.
My questions?
1. I do not know why but the copper is flaking off, or even Peeling off? and the plating solution is turning dark green, sometimes even blackish
green?
2. Can 1% sulf acid disolve the sulphide ore? How long does it take?
3. How do I extract the Silver? Will the sulf acid disolve the silver?
4. How do I extract the Lead?
Sorry for all the questions.
All the best!
Angela
|
|
not_important
International Hazard
Posts: 3873
Registered: 21-7-2006
Member Is Offline
Mood: No Mood
|
|
I think you want the thread over here http://www.sciencemadness.org/talk/viewthread.php?tid=9565
Quote: | Can 1% sulf acid disolve the sulphide ore? |
Sulfides should be oxidised before acid extraction, cold 1% H2SO4 isn't going to a lot to the sulfides of the metals in this. See this patent http://www.freepatentsonline.com/EP1303642.html
Treat the reside with Na2CO3 aq to convert lead sulfate to the carbonate. Extract with HNO3 to dissolve both lead and silver.
|
|
dale_wilson69
Harmless
Posts: 12
Registered: 1-12-2007
Member Is Offline
Mood: No Mood
|
|
Thanks not_important, but you are important to me. Thanks for the help.
I was told if I mill the ore down to micron size I could extract the copper from the sulfides using 1-1.5% sulf acid. Is that true?
|
|
angela_li
Harmless
Posts: 8
Registered: 3-12-2007
Member Is Offline
Mood: No Mood
|
|
Sorry Dale. I think you answered the wrong person.
But thanks for the post.
Angela.
|
|
angela_li
Harmless
Posts: 8
Registered: 3-12-2007
Member Is Offline
Mood: No Mood
|
|
I wish to thank not_important for the help. I think I found the answer. I was using 304 stainless steel and 99.99% lead. I should have been using
316 stainless steel and lead containing Pb, Ca, Sn, and Ag.
All the best !
Angela
|
|
angela_li
Harmless
Posts: 8
Registered: 3-12-2007
Member Is Offline
Mood: No Mood
|
|
Help.
Can 1 - 1.5% sulf acid disolve copper and silver in oxide and sulphide ore, if the ore is mill to micron size?
|
|