Liquid sodium hydroxide and aluminum?
Does aluminum react with molten sodium hydroxide, and what is the equation? Do metals react with sodium hydroxide to make metal hydroxides? Like zinc
and NaOH makes zinc hydroxide... I read that it's possible to make sodium this way, because reacting aluminum with aqueous sodium hydroxide, the
sodium just reacts with the water and goes away. If it works, I'm going to melt some sodium hydroxide with a meker burner, but I'm afraid it will ruin
the glass. Would it work with a copper container?
[Edited on 29-5-2013 by Cou]
|
|
|
elementcollector1
International Hazard
Posts: 2684
Registered: 28-12-2011
Location: The Known Universe
Member Is Offline
Mood: Molten
|
|
Yes, look it up (it makes sodium aluminate), depends on whether they're amphoteric or not, it's more of a thermite-style reaction than a molten thing
(don't play with molten hydroxide! It will murderify you and make you dead!), and maybe (I've seen sodium cuprate, so no promises).
Elements Collected:52/87
Latest Acquired: Cl
Next in Line: Nd
|
|
|
blogfast25
International Hazard
Posts: 10562
Registered: 3-2-2008
Location: Neverland
Member Is Offline
Mood: No Mood
|
|
Quote: Originally posted by Cou  | If it works, I'm going to melt some sodium hydroxide with a meker burner, but I'm afraid it will ruin the glass. Would it work with a copper
container?
[Edited on 29-5-2013 by Cou] |
By NO MEANS add aluminium to an NaOH melt, as a violent reaction will result.
As for making sodium from NaOH + 2/3 Al === > Na + 1/3 Al2O3 + 1/2 H2, it isn't worth doing. Read the other thread currently active on 'chemical'
sodium.
If you're going to mess with molten NaOH, electrolysing it would be safer and easier.
|
|
|
Fantasma4500
International Hazard
Posts: 1677
Registered: 12-12-2012
Location: Dysrope (aka europe)
Member Is Offline
Mood: dangerously practical
|
|
if you want to try this at really small scale take aluminium and melt NaOH in.. sounds interesting.. sadly my carpet very very easily melts.. S:
|
|
|
Bot0nist
International Hazard
Posts: 1559
Registered: 15-2-2011
Location: Right behind you.
Member Is Offline
Mood: Streching my cotyledons.
|
|
Oh, and dont melt NaOH in glass! It will digest it. use a suitable metal contianer or crucible...
U.T.F.S.E. and learn the joys of autodidacticism!
Don't judge each day only by the harvest you reap, but also by the seeds you sow.
|
|
|
ScienceSquirrel
International Hazard
Posts: 1863
Registered: 18-6-2008
Location: Brittany
Member Is Offline
Mood: Dogs are pets but cats are little furry humans with four feet and self determination! 
|
|
Aluminium reacts quite readily with solutions of alkali.
Adding it to molten sodium hydroxide will result in a violent reaction that could be extremely dangerous.
|
|
|
kristofvagyok
National Hazard
Posts: 659
Registered: 6-4-2012
Location: Europe
Member Is Offline
Mood: No Mood
|
|
Sodium and potassium hydroxide could be melt in a silver pot. Do not even try aluminium, it will end up as a really nasty accident.
I have a blog where I post my pictures from my work: http://labphoto.tumblr.com/
-Pictures from chemistry, check it out(:
"You can’t become a chemist and expect to live forever." |
|
|
Cou
National Hazard
Posts: 958
Registered: 16-5-2013
Member Is Offline
Mood: Mad Scientist
|
|
Well i'm sticking to just electrolysis of molten NaOH and KOH now
|
|
|
Metacelsus
International Hazard
Posts: 2532
Registered: 26-12-2012
Location: Boston, MA
Member Is Offline
Mood: Double, double, toil and trouble
|
|
Electrolysis of molten KOH doesn't work; the K dissolves in the molten KOH.
|
|
|
Finnnicus
Hazard to Others
Posts: 342
Registered: 22-3-2013
Member Is Offline
|
|
Nickel! Nickel is the way to go vs strong bases. Even an electroplated layer works great.
|
|
|
blogfast25
International Hazard
Posts: 10562
Registered: 3-2-2008
Location: Neverland
Member Is Offline
Mood: No Mood
|
|
Hmmm... up to the 50s electrolytic K (from KOH) was the prevailing production method.
|
|
|
Eddygp
National Hazard
Posts: 858
Registered: 31-3-2012
Location: University of York, UK
Member Is Offline
Mood: Organometallic
|
|
Don't mix aluminium with molten NaOH!!! Your neighbours have the right to live!!
It forms sodium aluminate. However, I suggest you do that as wet chemistry. A conc. solution of NaOH with Al will follow the next reaction:
NaOH + Al + H2O = NaAlO2 + 3/2 H2
there may be bugs in gfind
[ˌɛdidʒiˈpiː] IPA pronunciation for my Username |
|
|
Bot0nist
International Hazard
Posts: 1559
Registered: 15-2-2011
Location: Right behind you.
Member Is Offline
Mood: Streching my cotyledons.
|
|
| Quote: Originally posted by Eddygp | Don't mix aluminium with molten NaOH!!! Your neighbours have the right to live!!
It forms sodium aluminate. However, I suggest you do that as wet chemistry. A conc. solution of NaOH with Al will follow the next reaction:
NaOH + Al + H2O = NaAlO2 + 3/2 H2 |
I've done said reaction. It works fine, however, keep in mind that the formed NaAlO<sub>2</sub> will be a gel (per usual) and the hydrogen
gas being produced will be full of caustic aerosol, so don't stream it straight into a balloon or breath it. The caustic aerosol is very irritating,
and can easily fill a small room, even when just dissolving some foil pieces in 100ml of conc. NaOH solution.
Be careful if you do decide to experiment with molten sodium or potassium hydroxide. It is very nasty stuff and will hurt you badly. There are some
cool videos on YouTube showing it dissolving a beaker almost instantly. Scary, scary stuff if you haven't the experience, respect and equipment to
handle it safely.
U.T.F.S.E. and learn the joys of autodidacticism!
Don't judge each day only by the harvest you reap, but also by the seeds you sow.
|
|
|
Fantasma4500
International Hazard
Posts: 1677
Registered: 12-12-2012
Location: Dysrope (aka europe)
Member Is Offline
Mood: dangerously practical
|
|
just to add....
316 steel IIRC can withstand molten hydroxides.. remember this from one of nurdrages early videos
|
|
|
Bot0nist
International Hazard
Posts: 1559
Registered: 15-2-2011
Location: Right behind you.
Member Is Offline
Mood: Streching my cotyledons.
|
|
Thats the video I recal as well. Doesn't hold up like nickel or silver, of course, but if its a pan you dont care to much about, give it a shot. I
imagine it will corrode or pit it some. I have never tried it myself though...
U.T.F.S.E. and learn the joys of autodidacticism!
Don't judge each day only by the harvest you reap, but also by the seeds you sow.
|
|
|
DrSchnufflez
Hazard to Others
Posts: 114
Registered: 22-1-2013
Location: Australia
Member Is Offline
Mood: No Mood
|
|
I use stainless steel measuring cups that I bought for $4 from a kitchen shop. They have been in contact for 3-4 hours with molten hydroxide and show
no pitting, just darkening. 
|
|
|
hyfalcon
International Hazard
Posts: 1003
Registered: 29-3-2012
Member Is Offline
Mood: No Mood
|
|
It's the nickel in the stainless that makes it resistant.
|
|
|
Fantasma4500
International Hazard
Posts: 1677
Registered: 12-12-2012
Location: Dysrope (aka europe)
Member Is Offline
Mood: dangerously practical
|
|
i believe the etching of steel (316?) will be as little as only few millimetres PER YEAR of exposure to molten NaOH
anyhow i got some news for the OP...
i tested this out.. i took first aluminium foil.. didnt do something interesting.. left a hole and suddenly there was no liquid but seemingly nothing
left at all..
i then put NaOH pellets on a CPU aluminium cooler and heated..
suddenly a reaction occured!
it was like a tiny little flash, definately very energetic for the simplicity of the reaction..
it was like a yellow flash, like a little poof as you know it from granulated BP (if you do..)
in larger scale this COULD potentially be dangerous
when the small flash has occured a solid remains, plain white and instantly solidifies and flattens out at once
doubt this is sodium metal tho.. but very interesting what so ever
safety lies within amounts used
|
|
|
blogfast25
International Hazard
Posts: 10562
Registered: 3-2-2008
Location: Neverland
Member Is Offline
Mood: No Mood
|
|
Nope. About 11 % of chromium. Assuming by 'stainless' you are referring to Stainless Steel aka Inox.
|
|
|
kmno4
International Hazard
Posts: 1495
Registered: 1-6-2005
Location: Silly, stupid country
Member Is Offline
Mood: No Mood
|
|
Interesting papers:
| Code: | http://www.electrochem.org/dl/ma/201/pdfs/1433.pdf |
and
| Code: | http://link.springer.com/article/10.1007%2FBF00774695 |
See also Mellor vol.5, p.217
Seems that vigorous reaction is caused by H2O from commercial NaOH. So before experiment NaOH should be melted and dehydrated.
Hm....
[Edited on 31-5-2013 by kmno4]
Слава Україні !
Героям слава !
|
|
|
Fantasma4500
International Hazard
Posts: 1677
Registered: 12-12-2012
Location: Dysrope (aka europe)
Member Is Offline
Mood: dangerously practical
|
|
| Quote: Originally posted by kmno4 | Interesting papers:
| Code: | http://www.electrochem.org/dl/ma/201/pdfs/1433.pdf |
and
| Code: | http://link.springer.com/article/10.1007%2FBF00774695 |
See also Mellor vol.5, p.217
Seems that vigorous reaction is caused by H2O from commercial NaOH. So before experiment NaOH should be melted and dehydrated.
Hm....
[Edited on 31-5-2013 by kmno4] |
i did try to use the pellets for dragging water out of certain things as in dessication, but didnt seem very strong of a dessicant..
i did however see on the aluminium that after some time the 3 pellets which were melted started to get wet?
i think youre right that theres water in the NaOH.. problem is just that i would need some good steel to 100% dehydrate it..
interesting links.. seem illogical to me that titanium would get etched many many times faster than magnesium and aluminium (and magnesium getting
etched slower..?)
|
|
|
hyfalcon
International Hazard
Posts: 1003
Registered: 29-3-2012
Member Is Offline
Mood: No Mood
|
|
There's that also. It's the nickel that's resistant to the NaOH though.
I've studied the Franklin battery to much not to know that.
|
|
|
Surrealist
Harmless
Posts: 5
Registered: 6-6-2018
Member Is Offline
|
|
I tried this and had a much less exciting result than anticipated. 210 g NaOH was heated to the melting point in a stainless steel pot along with
aluminum foil pieces totaling 0.5 g. After fifteen minutes, it was molten and the aluminum still shiny. 0.9 g magnesium (one whole piece) to this, and
it bubbled with a white halo. This is a good start to confirming that the aluminum may simply passivate too quickly for this to be any good. After two
hours, the aluminum was still shiny! Another 27 g aluminum foil was added loosely on top and waited for another hour. No violent reaction occured.
28.5 g of aluminum coated with oxides and sodium hydroxide was easily removed, while the hydroxide “layer” seemed to encase the aluminum and make
it very brittle and white. After washing with water very slowly and carefully and adding the solution to the appropriate waste container, the
magnesium chunk was even able to be removed, although it was black in some places and now only weighed 0.75g. The stainless steel lid was on the pot
at all times except when pictures were taken. It was quite shocking that the $15 hotplate from walmart managed to melt sodium hydroxide (mp 318 C) in
the first place. Mineral oil boils at 310 C, just shy of being able to hold molten sodium hydroxide but high enough to handle the potassium sodium
hydroxide eutectic. (mp 170 C, .515:.485 Na:K molar ratio) and (218 C, .373:.627 Na:K molar ratio)
http://www.crct.polymtl.ca/fact/phase_diagram.php?file=KOH-NaOH.jpg&dir=FTsalt Mineral oil could shield this from the air. Some amalgamation might
help the process along. Mercury boils at 357 C. Ill post what happens with this eutectic, amalgamated, protected experiment when I try it, but Ill
need to get the mercury from its sulfide first.
|
|
|
AJKOER
Radically Dubious
Posts: 3026
Registered: 7-5-2011
Member Is Offline
Mood: No Mood
|
|
Sodium aluminate formula is given variously as NaAlO2, NaAl(OH)4 (upon hydration); Na2O·Al2O3, or Na2Al2O4 (see https://en.wikipedia.org/wiki/Sodium_aluminate#Reaction_of_a...).
To prepare NaAl(OH)4, the requested reaction with NaOH is:
Al + NaOH + 3 H2O --> NaAl(OH)4 + 3/2 H2 (g)
or, upon scaling:
2 Al + 2 NaOH + 6 H2O --> 2 NaAl(OH)4 + 3 H2 (g)
However, one does not actually need NaOH here as heating aqueous NaHCO3 with added aluminum foil also creates sodium aluminate and hydrogen gas, as I
have done. The reason is hot aqueous NaHCO3 acts like NaOH and will attack aluminum items placed, for example, in a disk washer using sodium
bicarbonate per the reaction:
NaHCO3 + H2O + Heat --> H2O + CO2 (g) + NaOH
Or, more generally, the equilibrium (which may be moved to the right as claimed above) is given by:
HCO3− + H2O = H2CO3 + OH− (see https://en.wikipedia.org/wiki/Sodium_bicarbonate )
As NaHCO3 is amphoteric, a possible reaction with the aluminate releasing Al(OH)3:
NaHCO3 + NaAl(OH)4 = Na2CO3 + Al(OH)3 (s) + H2O
Interestingly, aluminum hydroxide is also amphoteric (see http://www.oneonta.edu/faculty/kotzjc/LAB/Complexation.pdf ):
[Al(H2O)3(OH)3] (s) + 3 H3O+ --> [Al(H2O)6]3+ (aq) + 3 H2O
[Al(H2O)3(OH)3] (s) + OH- --> [Al(H2O)2(OH)4]- (aq) + H2O
[Edited on 16-6-2018 by AJKOER]
|
|
|